Because we make the Silver and Super Surfers, one can get as large or small a blow made as they want for their Elev8 vaporizer. 29mm SSV large wand and heater cover 19mm female conical wand is larger than a spherical flavor disc wand Or we have a small dosing wand to even work with …
Not really, a scratch will boil and just get worse. Also, any heat work could cause a piece to break, so it is best to leave it. Once and do a polish, but this is time-consuming and not what Elev8 Premier does.
We are not doctors, so we do not fully know. What we have concluded by research is that the actual smoke particles are larger than the vapor particles. Making it easier to absorb vapor over smoke.
Yes, we can sandblast a standard Elev8 piece of glass. Scratched glass has worked with us before, but we can also do it in-house.
It all comes down to the user. Some users want big hits, others want small hits. You like what you like, so find your sweet spot. Concentrates will vape at a lower setting than the flower setting. This is because the heater is directly touching the quartz, and for flower the air has to heat …
The SideKick V1 uses two batteries in series to get 8.4 volts. This allows the heater to heat up much faster. The SK V2 uses 1 battery that has much more potential power, but because it is 1 battery, it is 3.7 volts. Even though the SK heats up a bit slower, it can run …
Yes, the Silver Surfer may have been the first E-Nail on the market. We had not seen one until years after the first SSV EOK dab dish. The heater had a titanium dish that one would put their dabs into. Later we found out that TI oxidizes very fast at a high temperature and can …
Continue reading “has there ever been a titanium attachment for the ssv eok kit?”
There are two types of quartz. Quartz crystal, which can be natural or lab-grown, or fused silica which is quartz glass.
The ceramic heater can get up to 900 degrees. The heater has a 3 year warranty and some heaters have been working 15+ years.
It is a small layer of protective oxide that is produced by an electrolytic processes